LLDPE TUFLIN™ HSE-1003 NT 7

TUFLIN™ HSE-1003 NT 7

TUFLIN™ HSE-1003 NT 7

LLDPE

陶氏化学(Dow Chemical)

产品描述

TUFLIN™ HSE-1003 NT 7 Linear Low Density Polyethylene Resin is an ethylene-hexene-1 copolymer designed for cast stretch film applications such as industrial pallet wrap. Films containing HSE-1003 offer outstanding puncture, toughness and load holding properties.


  • Industrial pallet wrap stretch film applications

  • Premium film packaging applications

  • Complies with U.S. FDA 21 CFR 177.1520 (c) 3.1a

  • Consult the regulations for complete details.

    基本信息
    原厂资料
    物性表(英文)
    法规认证
    FDA(食品药品监督管理局)
    成型方式
    流延薄膜
    技术参数
    物理性能 值/单位 测试标准 测试条件

    密度

    0.918 g/cm³ ASTM D792

    密度

    0.918 g/cm³ Internal
    Base Density

    熔体质量流动速率(MFR)

    190℃/2.16 kg

    2.5 g/10min ASTM D1238
    热学性能 值/单位 测试标准 测试条件

    维卡软化温度(Vicat)

    98.9 °C ASTM D1525

    熔融温度(Tm)

    124 °C Internal
    DSC

    加工温度

    274 °C -
    Melt Temperature
    光学性能 值/单位 测试标准 测试条件

    雾度

    1 % ASTM D1003
    20.3 µm

    雾度

    4 % ASTM D1003
    50.8 µm

    光泽度

    95 - ASTM D 2457
    20.3 µm

    光泽度

    156 - ASTM D 2457
    20.3 µm

    光泽度

    91 - ASTM D 2457
    50.8 µm

    光泽度

    146 - ASTM D 2457
    50.8 µm
    薄膜性能 值/单位 测试标准 测试条件

    拉伸强度

    屈服(yld)

    11.2 Mpa ASTM D 882
    MD, 20 µm

    屈服(yld)

    10.2 Mpa ASTM D 882
    MD, 51 µm

    屈服(yld)

    10.5 Mpa ASTM D 882
    TD, 20 µm

    屈服(yld)

    9.98 Mpa ASTM D 882
    TD, 51 µm

    断裂(brk)

    49.8 Mpa ASTM D 882
    MD, 20 µm

    断裂(brk)

    38.4 Mpa ASTM D 882
    MD, 51 µm

    断裂(brk)

    36.1 Mpa ASTM D 882
    TD, 20 µm

    断裂(brk)

    44.2 Mpa ASTM D 882
    TD, 51 µm

    拉伸延伸率

    断裂(brk)

    520 % ASTM D 882
    MD, 20 µm

    断裂(brk)

    720 % ASTM D 882
    MD, 51 µm

    断裂(brk)

    830 % ASTM D 882
    TD, 20 µm

    断裂(brk)

    900 % ASTM D 882
    TD, 51 µm

    穿透强度

    40 N Internal
    20 µm

    穿透强度

    84.5 N Internal
    51 µm

    耐穿透性

    26.4 J/cm³ Internal
    20 µm

    耐穿透性

    3.84 J Internal
    20 µm

    耐穿透性

    20.8 J/cm³ Internal
    51 µm

    耐穿透性

    8.25 J Internal
    51 µm

    抗拉韧性

    209 J/cm³ ASTM D882
    MD, 20 µm

    抗拉韧性

    255 J/cm³ ASTM D882
    MD, 51 µm

    抗拉韧性

    269 J/cm³ ASTM D882
    TD, 20 µm

    抗拉韧性

    334 J/cm³ ASTM D882
    TD, 51 µm

    埃尔曼多夫撕裂

    180 g ASTM D 1922
    MD, 20 µm

    埃尔曼多夫撕裂

    780 g ASTM D 1922
    MD, 51 µm

    埃尔曼多夫撕裂

    620 g ASTM D 1922
    TD, 20 µm

    埃尔曼多夫撕裂

    1100 g ASTM D 1922
    TD, 51 µm

    割线模量

    147 Mpa ASTM D 882
    2% Secant, MD, 20 µm

    割线模量

    142 Mpa ASTM D 882
    2% Secant, MD, 51 µm

    割线模量

    156 Mpa ASTM D 882
    2% Secant, TD, 20 µm

    割线模量

    142 Mpa ASTM D 882
    2% Secant, TD, 51 µm

    落锤冲击

    130 g ASTM D 1709
    20 µm, A

    落锤冲击

    100 g ASTM D 1709
    20 µm, B

    落锤冲击

    270 g ASTM D 1709
    51 µm, A

    落锤冲击

    170 g ASTM D 1709
    51 µm, B