ExxonMobil™ LLDPE LL 1001BU
LLDPE
埃克森美孚化工(ExxonMobil Chemical)
产品描述
ExxonMobil™ LL 1001BU resin offers excellent drawdown and puncture resistance combined with high gloss and clarity. It is frequently used as a blend partner with LDPE resins to improve film properties and processability. TnPP is not intentionally added to LL 1001BU resin.
基本信息
| 原厂资料 | 物性表(英文) 物性表(中文) | |||
| 添加助剂 | 热稳定剂增滑剂开口剂 | |||
| 颜色形状 | 粒状 | |||
| 成型方式 | 薄膜挤出吹膜 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.918 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 1 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 98 °C | Internal | |
熔融温度(Tm) | 122 °C | Internal | Peak |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 13 % | ASTM D1003 | |
光泽度 | 53 - | ASTM D 2457 | 45° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 9.3 Mpa | ASTM D 882 | MD |
屈服(yld) | 9.7 Mpa | ASTM D 882 | TD |
断裂(brk) | 44 Mpa | ASTM D 882 | MD |
断裂(brk) | 26 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 510 % | ASTM D 882 | MD |
断裂(brk) | 690 % | ASTM D 882 | TD |
穿透强度 | 26 N | Internal | |
耐穿透性 | 1.1 J | Internal | |
埃尔曼多夫撕裂 | 100 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 450 g | ASTM D 1922 | TD |
割线模量 | 170 Mpa | ASTM D 882 | 1% Secant, MD |
割线模量 | 190 Mpa | ASTM D 882 | 1% Secant, TD |
落锤冲击 | 80 g | ASTM D 1709 |