Marlex® 7308DL
LLDPE
雪佛龙菲利普斯(Chevron Phillips)
产品描述
This linear low density polyethylene is an ethylene-hexene copolymer tailored for blown film applications that require:
• Good toughness properties
• Increased stiffness
• Low creep
• Good drawdown
• Excellent processing characteristics
• Use alone or in coextrusions; blends with other polyolefins
Typical blown film applications include:
• Industrial films and bags that require added stiffness
• Thin gauge applications
• General purpose packaging
基本信息
| 原厂资料 | 物性表(英文) | |||
| 添加助剂 | 加工助剂开口剂 | |||
| 成型方式 | 吹膜 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.925 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.8 g/10min | ASTM D1238 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
摩擦系数 | 0.5 - | ASTM 1894 | 1 mil Blown Film |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 22 % | ASTM D1003 | 1 mil Blown Film |
光泽度 | 55 - | ASTM D 2457 | 60°, 1 mil Blown Film |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 55 Mpa | ASTM D 882 | MD, 1 mil Blown Film |
断裂(brk) | 34 Mpa | ASTM D 882 | TD, 1 mil Blown Film |
拉伸延伸率 | |||
断裂(brk) | 400 % | ASTM D 882 | MD, 1 mil Blown Film |
断裂(brk) | 600 % | ASTM D 882 | TD, 1 mil Blown Film |
埃尔曼多夫撕裂 | 300 g/mil | ASTM D 1922 | MD, 1 mil Blown Film |
埃尔曼多夫撕裂 | 650 g/mil | ASTM D 1922 | TD, 1 mil Blown Film |
割线模量 | 276 Mpa | ASTM D 882 | 1 % Secant, MD, 1 mil Blown Film |
割线模量 | 324 Mpa | ASTM D 882 | 1 % Secant, TD, 1 mil Blown Film |
落锤冲击 | 125 g/mil | ASTM D 1709 | 1 mil Blown Film |