DOWLEX™ GM 8071G
LLDPE
陶氏化学(Dow Chemical)
产品描述
DOWLEX™ GM 8071G Polyethylene Resin is designed for use in a wide variety of film applications, in special for high strength consumer trash bags/liners. This product can be used in other applications that require toughness and also offers great melt strength for high throughput rates.
Main Characteristics
High toughness, processability and good optical properties
Complies with:
U.S. FDA FCN 741
Canadian HPFB No Objection
Consult the regulations for complete details
基本信息
原厂资料 | 物性表(英文) | |||
法规认证 | FDA(食品药品监督管理局)HPFB (加拿大健康产品和食品局) |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 0.92 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.9 g/10min | ASTM D1238 | |
热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 106 °C | ASTM D1525 | |
熔融温度(Tm) | 118 °C | Internal | DSC |
光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 16.7 % | ASTM D1003 | 20.3 µm |
光泽度 | 45 - | ASTM D 2457 | 45°,20.3 µm |
薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 9.38 Mpa | ASTM D 882 | MD |
屈服(yld) | 9.38 Mpa | ASTM D 882 | TD |
断裂(brk) | 29.1 Mpa | ASTM D 882 | MD |
断裂(brk) | 20.7 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 420 % | ASTM D 882 | MD |
断裂(brk) | 500 % | ASTM D 882 | TD |
耐穿透性 | 13.4 J/cm³ | Internal | 23 µm |
埃尔曼多夫撕裂 | 330 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 490 g | ASTM D 1922 | TD |
割线模量 | 171 Mpa | ASTM D 882 | 2% Secant, MD |
割线模量 | 187 Mpa | ASTM D 882 | 2% Secant, TD |
落锤冲击 | 670 g | ASTM D 1709 |