ICORENE® 3560 is a polyethylene developed for rotational molding applications. Intended applications are primarily large hollow objects, including toys, playground equipment, and a variety of other products.
ICORENE® 3560 is a linear low density polyethylene specifically developed for rotational moulding.
This grade is suitable for use in general purpose applications. It has a good balance of properties such as toughness, easy flow and stiffness.
基本信息
| 原厂资料 | 物性表-ASTM(英文) 物性表(英文) | |||
| 产品特性 | 良好的刚性耐低温冲击高韧性易成型抗紫外线良好流动性 | |||
| 添加助剂 | 紫外线稳定剂 | |||
| 颜色形状 | 粒状粉末状本色黑色 | |||
| 成型方式 | 滚塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.935 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 5 g/10min | ASTM D1238 | |
190℃/2.16 kg | 6.7 g/10min | ASTM D1238 | |
环境应力开裂(ESCR ) | 50 Hours | ASTM D 1693 | 10% Igepal, F50 |
环境应力开裂(ESCR ) | 1000 Hours | ASTM D 1693 | 100% Igepal, F50 |
环境应力开裂(ESCR ) | 150 Hours | ASTM D 1693 | 50°C, 100% Igepal, F50 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 17 Mpa | ASTM D638 | |
屈服(yld) | 18.3 Mpa | ASTM D638 | 51 mm/min |
弯曲模量 | 696 Mpa | ASTM D790 | |
弯曲模量 | 550 Mpa | ISO 178 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
落锤冲击 | 170 J/cm | Internal | -20°C |
落锤冲击 | 71 J | Internal | -40°C, 3.18 mm, Rotational Molded |
落锤冲击 | 217 J | Internal | -40°C, 6.35 mm, Rotational Molded |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 55 D | ASTM D 2240 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 52 °C | ASTM D648 | Unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 54.4 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 36 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 38.3 °C | ASTM D648 | Unannealed |
熔融温度(Tm) | 125 °C | ASTM D3418 |