DOWLEX™ 2036.01G
LLDPE
陶氏化学(Dow Chemical)
产品描述
DOWLEX™ 2036.01G Linear Low Density Polyethylene Resin is suitable for the production of cast films with high stiffness, good tear strength and outstanding toughness. It can be used in skin layers of coextreuded cast films made from DOWLEX resins to provide a surface with good slip properties.
Complies with:
EU, N0 10/2011
FDA 21 CRF 177.1520(c) 3.2a.
Consult the regulations for complete details.
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 成型方式 | 流延薄膜 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.933 g/cm³ | ASTM D792 | |
密度 | 0.935 g/cm³ | Internal | Base Density |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 2.5 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 119 °C | ASTM D1525 | |
熔融温度(Tm) | 125 °C | Internal | DSC |
加工温度 | 274 °C | - | Extrusion |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 2.6 % | ASTM D1003 | |
光泽度 | 90 - | ASTM D 2457 | 45° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 16.9 Mpa | ASTM D 882 | MD |
屈服(yld) | 17.6 Mpa | ASTM D 882 | TD |
断裂(brk) | 59.2 Mpa | ASTM D 882 | MD |
断裂(brk) | 39.9 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 620 % | ASTM D 882 | MD |
断裂(brk) | 750 % | ASTM D 882 | TD |
耐穿透性 | 10.3 J/cm³ | Internal | |
抗拉韧性 | 324 J/cm³ | ASTM D882 | MD |
抗拉韧性 | 308 J/cm³ | ASTM D882 | TD |
埃尔曼多夫撕裂 | 83 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 290 g | ASTM D 1922 | TD |
落锤冲击 | 57 g | ASTM D 1709 |