LLDPE DOW™ LLDPE GRSN-9820 NT 7

DOW™ LLDPE GRSN-9820 NT 7

DOW™ LLDPE GRSN-9820 NT 7

LLDPE

陶氏化学(Dow Chemical)

产品描述

DOW GRSN-9820 NT 7 Linear Low Density Polyethylene (LLDPE) Resin is produced using UNIPOL™ PE Process Technology and is supplied in granular form. This resin is specifically designed as a carrier resin for color concentrates and other masterbatch systems. The fine particle size reduces the need for grinding, and the high surface area of granular resin allows for more uniform dispersion of concentrate in the final product. GRSN-9820 NT 7 is compatible with polyethylene and polypropylene resins and can be used in a wide variety of fabrication processes.

  • Granular form

  • Carrier resin for masterbatch systems

  • Complies with U.S. FDA 21 CFR 177.1520 (c)3.1a

  • Complies with EU, No 10/2011

  • Consult the regulations for complete details.

    基本信息
    原厂资料
    物性表-ASTM(英文)
    法规认证
    EU Food Contact(2011/10/EC)(欧盟食品级)
    RoHS(欧盟电子电气设备中有害物质)
    成型方式
    共混改性
    技术参数
    物理性能 值/单位 测试标准 测试条件

    密度

    0.924 g/cm³ ASTM D792

    密度

    0.924 g/cm³ Internal
    Base Density

    熔体质量流动速率(MFR)

    190℃/2.16 kg

    20 g/10min ASTM D1238

    环境应力开裂(ESCR )

    20 Hours ASTM D 1693
    50°C, 100% Igepal, F50
    机械性能 值/单位 测试标准 测试条件

    拉伸强度

    屈服(yld)

    11.7 Mpa ASTM D638

    断裂(brk)

    7.58 Mpa ASTM D638

    拉伸延伸率

    屈服(yld)

    3 % ASTM D638

    断裂(brk)

    60 % ASTM D638

    弯曲模量

    386 Mpa ASTM D790
    2% Secant
    冲击性能 值/单位 测试标准 测试条件

    拉伸冲击

    168 kJ/m² ASTM D 1822
    Type S

    脆化温度

    -76.1 °C ASTM D 746
    硬度性能 值/单位 测试标准 测试条件

    邵氏硬度 D

    50 D ASTM D 2240
    热学性能 值/单位 测试标准 测试条件

    热变形温度(HDT)

    0.45 Mpa (66 psi)(4.6kg/cm²)

    42.8 °C ASTM D648
    Unannealed

    维卡软化温度(Vicat)

    93.9 °C ASTM D1525

    熔融温度(Tm)

    123 °C Internal
    DSC

    结晶温度

    108 °C Internal
    DSC