POLYAXIS® CP 812
LLDPE
利安德巴塞尔(LyondellBasell)
产品描述
Polyaxis CP 812 is a general purpose linear low density polyethylene compund offering quick cycles and part to part consistancy. Available as pellet or powder.
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 产品特性 | 短周期成型抗紫外线 | |||
| 添加助剂 | 紫外线稳定剂 | |||
| 颜色形状 | 粒状粉末状可定制色 | |||
| 成型方式 | 滚塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.932~0.939 g/cm³ | ASTM D 1505 | Compression Molded |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 5~7 g/10min | ASTM D1238 | |
环境应力开裂(ESCR ) | 25 Hours | ASTM D 1693 | 10% Igepal, Compression Molded, F50 |
环境应力开裂(ESCR ) | 500 Hours | ASTM D 1693 | 100% Igepal, Compression Molded, F50 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 15.5 Mpa | ASTM D638 | 51 mm/min, Rotational Molded |
拉伸延伸率 | |||
断裂(brk) | 500 % | ASTM D638 | 51 mm/min, Rotational Molded |
弯曲模量 | 586 Mpa | ASTM D790 | 1% Secant, Rotational Molded |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
落锤冲击 | 76 J | Internal | -40°C, 3.18 mm, Rotational Molded |
落锤冲击 | 179 J | Internal | -40°C, 6.35 mm, Rotational Molded |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 54 °C | ASTM D648 | Unannealed, 0.125 mm, Rotational Molded |
1.8 Mpa (264 psi)（18.6kg/cm²） | 36 °C | ASTM D648 | Unannealed, 0.125 mm, Rotational Molded |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 | ALL |