LLDPE Lotrène® LLDPE Q2018H

Lotrène® LLDPE Q2018H

Lotrène® LLDPE Q2018H

LLDPE

卡塔尔石化/梦塔佳(Muntajat)

产品描述

Lotrène® Q2018 Series are Linear Low Density Polyethylene resins produced in a gas phase reactor using butene (C4) co-monomer.

They are designed for blown film applications and can be used in pure form as well as blended with other PE resins, such as LDPE or HDPE and mPE resins for mono extrusion or co-extrusion process to modify film properties.

Lotrène® Q2018 Series are suited for many applications in the field of consumer, industrial, food or hygiene packaging such as freezer film, bread bags, shoppers and bags as well as lamination film and multilayer packaging film.

基本信息
原厂资料
物性表(英文)
产品特性
食品接触级
添加助剂
增滑剂
开口剂
成型方式
薄膜挤出
吹膜
共挤
共混改性
应用产品
薄膜
塑料袋
共混
食品包装
包装
多层薄膜
复合膜
技术参数
物理性能 值/单位 测试标准 测试条件

密度

0.918 g/cm³ ASTM D792

熔体质量流动速率(MFR)

190℃/2.16 kg

2 g/10min ASTM D1238
热学性能 值/单位 测试标准 测试条件

维卡软化温度(Vicat)

100 °C ASTM D1525
A120

结晶温度

121 °C Internal
光学性能 值/单位 测试标准 测试条件

雾度

14 % ASTM D1003
40 µm, Blown Film

光泽度

55 - ASTM D 2457
45°, 40 µm, Blown Film
薄膜性能 值/单位 测试标准 测试条件

薄膜测试厚度

40 μm Internal
Blown Film

拉伸强度

屈服(yld)

11 Mpa ASTM D 882
MD

屈服(yld)

11 Mpa ASTM D 882
TD

断裂(brk)

32 Mpa ASTM D 882
MD

断裂(brk)

35 Mpa ASTM D 882
TD

拉伸延伸率

断裂(brk)

900 % ASTM D 882
MD

断裂(brk)

850 % ASTM D 882
TD

埃尔曼多夫撕裂

105 N/mm ASTM D 1922
MD

埃尔曼多夫撕裂

420 g ASTM D 1922
MD

埃尔曼多夫撕裂

55 N/mm ASTM D 1922
TD

埃尔曼多夫撕裂

220 g ASTM D 1922
TD

割线模量

245 Mpa ASTM D 882
MD,1% Secant

割线模量

215 Mpa ASTM D 882
TD, 1% Secant

落锤冲击

130 g ASTM D 1709
F50