DOWLEX™ SC 2107GS
LLDPE
陶氏化学(Dow Chemical)
产品描述
DOWLEX™ SC 2107GS is ultra low gel ethylene octene copolymer. Films made from DOWLEX SC 2107GS Polyethylene Resin is processable at high line speeds, exhibits excellent stretchability, outstanding tear and impact resistance, as well as exceptional optical properties.
Main Characteristics:
Linear Low Density Polyethylene
Applications:
Industrial film
Hygiene & Medical film
Complies with:
U.S. FDA FCN 424
EU, No 10/2011
Consult the regulations for complete details.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 法规认证 | EU Food Contact(2011/10/EC)(欧盟食品级)FDA(食品药品监督管理局) | |||
| 成型方式 | 流延薄膜 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.917 g/cm³ | ASTM D792 | |
密度 | 0.917 g/cm³ | Internal | Base Density |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 2.3 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
加工温度 | 220~280 °C | - | Extrusion |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 0.7 % | ASTM D1003 | 23 µm |
光泽度 | 92 - | ASTM D 2457 | 45°, 23 µm |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 6.3 Mpa | ASTM D 882 | MD, 23 µm |
屈服(yld) | 5.9 Mpa | ASTM D 882 | TD, 23 µm |
断裂(brk) | 43 Mpa | ASTM D 882 | MD, 23 µm |
断裂(brk) | 28 Mpa | ASTM D 882 | TD, 23 µm |
拉伸延伸率 | |||
断裂(brk) | 470 % | ASTM D 882 | MD, 23 µm |
断裂(brk) | 900 % | ASTM D 882 | TD, 23 µm |
埃尔曼多夫撕裂 | 410 g | ASTM D 1922 | MD, 23 µm |
埃尔曼多夫撕裂 | 540 g | ASTM D 1922 | TD, 23 µm |
落锤冲击 | 200 g | ASTM D 1709 | 23 µm |