DOWLEX™ HMS 8018
LLDPE
陶氏化学(Dow Chemical)
产品描述
DOWLEX HMS 8018 Polyethylene Resin is designed for uses in Heavy Duty Shipping Sack application, both in industrial and consumer segments. Films made from this resin exhibit a combination of excellent toughness and tear resistance. This product also delivers good processability.
Application:
Heavy Duty Industrial and Consumer Shipping Sacks
基本信息
| 原厂资料 | 物性表(英文) | |||
| 成型方式 | 吹膜 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.92 g/cm³ | ASTM D792 | |
密度 | 0.92 g/cm³ | Internal | Base Density |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.9 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 107 °C | ASTM D1525 | |
熔融温度(Tm) | 119 °C | Internal | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 16 % | ASTM D1003 | 25.4 µm |
雾度 | 8.8 % | ASTM D1003 | 50.8 µm |
光泽度 | 41 - | ASTM D 2457 | 45°, 25.4 µm |
光泽度 | 81 - | ASTM D 2457 | 45°, 50.8 µm |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 10.8 Mpa | ASTM D 882 | MD, 25 µm |
屈服(yld) | 11 Mpa | ASTM D 882 | MD, 51 µm |
屈服(yld) | 11.6 Mpa | ASTM D 882 | TD, 25 µm |
屈服(yld) | 10.9 Mpa | ASTM D 882 | TD, 51 µm |
断裂(brk) | 45.4 Mpa | ASTM D 882 | MD, 25 µm |
断裂(brk) | 37.7 Mpa | ASTM D 882 | MD, 51 µm |
断裂(brk) | 41.6 Mpa | ASTM D 882 | TD, 25 µm |
断裂(brk) | 41.9 Mpa | ASTM D 882 | TD, 51 µm |
拉伸延伸率 | |||
断裂(brk) | 570 % | ASTM D 882 | MD, 25 µm |
断裂(brk) | 580 % | ASTM D 882 | MD, 51 µm |
断裂(brk) | 750 % | ASTM D 882 | TD, 25 µm |
断裂(brk) | 720 % | ASTM D 882 | TD, 51 µm |
穿透强度 | 53.4 N | Internal | 25 µm |
耐穿透性 | 25.2 J/cm³ | Internal | 25 µm |
耐穿透性 | 4.97 J | Internal | 25 µm |
抗拉韧性 | 113 J/cm³ | ASTM D882 | MD, 25µm |
抗拉韧性 | 131 J/cm³ | ASTM D882 | TD, 25 µm |
埃尔曼多夫撕裂 | 360 g | ASTM D 1922 | MD, 25 µm |
埃尔曼多夫撕裂 | 850 g | ASTM D 1922 | MD, 51 µm |
埃尔曼多夫撕裂 | 640 g | ASTM D 1922 | TD, 25 µm |
埃尔曼多夫撕裂 | 1100 g | ASTM D 1922 | TD, 51 µm |
割线模量 | 235 Mpa | ASTM D 882 | 1% Secant, MD, 25 µm |
割线模量 | 265 Mpa | ASTM D 882 | 1% Secant, TD, 25 µm |
割线模量 | 207 Mpa | ASTM D 882 | 2% Secant, MD, 25 µm |
割线模量 | 173 Mpa | ASTM D 882 | 2% Secant, MD, 51 µm |
割线模量 | 225 Mpa | ASTM D 882 | 2% Secant, TD, 25 µm |
割线模量 | 181 Mpa | ASTM D 882 | 2% Secant, TD, 51 µm |
落锤冲击 | 210 g | ASTM D 1709 | 25 µm |
落锤冲击 | 340 g | ASTM D 1709 | 51 µm |