DOWLEX™ 2085G
LLDPE
陶氏化学(Dow Chemical)
产品描述
DOWLEX* 2085G Polyethylene Resin is an ethylene-octene copolymer designed for general purpose thin gauge film applications. It is perfect for high strength consumer trash bags/liners. This product can be used in other applications that require toughness and also offers good melt strength for high throughput rates.
Complies with:
U.S. FDA 21 CFR 177.1520 (c) 3.2a
Consult the regulations for complete details.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 添加助剂 | 增滑剂开口剂 | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
| 成型方式 | 吹膜 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.92 g/cm³ | ASTM D792 | |
密度 | 0.917 g/cm³ | Internal | Base Density |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.85 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 105 °C | ASTM D1525 | |
熔融温度(Tm) | 122 °C | Internal | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 23 % | ASTM D1003 | |
光泽度 | 30 - | ASTM D 2457 | 45° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 8.27 Mpa | ASTM D 882 | MD |
屈服(yld) | 8.96 Mpa | ASTM D 882 | TD |
断裂(brk) | 34.5 Mpa | ASTM D 882 | MD |
断裂(brk) | 27.6 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 450 % | ASTM D 882 | MD |
断裂(brk) | 600 % | ASTM D 882 | TD |
穿透强度 | 53.4 N | Internal | 25 µm |
耐穿透性 | 20.7 J/cm³ | Internal | 25 µm |
耐穿透性 | 3.95 J | Internal | 25 µm |
抗拉韧性 | 70.3 J/cm³ | ASTM D882 | MD |
抗拉韧性 | 82.7 J/cm³ | ASTM D882 | TD |
埃尔曼多夫撕裂 | 350 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 600 g | ASTM D 1922 | TD |
割线模量 | 172 Mpa | ASTM D 882 | 1% Secant, MD |
割线模量 | 179 Mpa | ASTM D 882 | 1% Secant, TD |
割线模量 | 152 Mpa | ASTM D 882 | 2% Secant, MD |
割线模量 | 159 Mpa | ASTM D 882 | 2% Secant, TD |
落锤冲击 | 800 g | ASTM D 1709 |