DOWLEX™ GM 8051
LLDPE
陶氏化学(Dow Chemical)
产品描述
DOWLEX™ GM 8051 Polyethylene Resin is designed for use in a wide variety of film applications, in special for FFS and lamination multilayered films combining excellent optical properties, mechanicals and an additive package designed to enhance COF stability.
Main Characteristics:
High toughness, processability and optical properties
Fully formulated, enhanced COF stability
Complies with:
U.S. FDA FCN 741
Consult the regulations for complete details.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 添加助剂 | 增滑剂开口剂 | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.921 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.9 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 108 °C | ASTM D1525 | |
熔融温度(Tm) | 121 °C | Internal | DSC |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 11.4 % | ASTM D1003 | 50 µm |
光泽度 | 63 - | ASTM D 2457 | 45°,50 µm |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 7.2 Mpa | ASTM D 882 | MD |
屈服(yld) | 7.4 Mpa | ASTM D 882 | TD |
断裂(brk) | 43.4 Mpa | ASTM D 882 | MD |
断裂(brk) | 39.3 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 830 % | ASTM D 882 | MD |
断裂(brk) | 850 % | ASTM D 882 | TD |
耐穿透性 | 28.6 J/cm³ | Internal | 50 µm |
埃尔曼多夫撕裂 | 740 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 890 g | ASTM D 1922 | TD |
割线模量 | 178 Mpa | ASTM D 882 | 2% Secant, MD |
割线模量 | 203 Mpa | ASTM D 882 | 2% Secant, TD |
落锤冲击 | 600 g | ASTM D 1709 |