Marlex® 7104
LLDPE
雪佛龙菲利普斯(Chevron Phillips)
产品描述
This linear low density, high molecular weight ethylenehexene copolymer is tailored for sheet and geomembrane applications that require:
• Outstanding ESCR
• Good melt strength
• Excellent flexibility
• Good processability
• Good gloss
• High coefficient of friction values
Typical geomembrane applications for 7104 include:
• Landfill covers
• Flat and round-die products
Typical sheet applications for 7104 include:
• Coextruded cap layers on HDPE
• Blends with HDPE
This resin meets these specifications:
• ASTM D4976 - PE 215
• FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per 21 CFR 176.170(c)
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 良好柔韧性高光泽防滑/高摩擦易成型ESCR高熔体强度 | |||
| 法规认证 | ASTM D4976(聚乙烯注塑和挤压材料标准)FDA(食品药品监督管理局) | |||
| 成型方式 | 挤出片材挤出共混改性 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.919 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.35 g/10min | ASTM D1238 | |
环境应力开裂(ESCR ) | 2000 Hours | ASTM D 1693 | Condition B (10 % Igepal), F50 |
环境应力开裂(ESCR ) | 2000 Hours | ASTM D 1693 | Condition C (100 % Igepal), F50 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 11 Mpa | ASTM D638 | 2 in/min, Type IV bar |
拉伸延伸率 | |||
断裂(brk) | 700 % | ASTM D638 | 2 in/min, Type IV bar |
弯曲模量 | 410 Mpa | ASTM D790 | Tangent - 16:1 span:depth, 0.5 in/min |
单点缺口稳定张拉荷载(SP-NCTL) | 1000 Hours | ASTM D5379 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
脆化温度 | -75 °C | ASTM D 746 | Type A, Type I specimen |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 51 D | ASTM D 2240 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 51 °C | ASTM D648 | Method A |
维卡软化温度(Vicat) | 100 °C | ASTM D1525 | Loading 1, Rate A |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
氧化诱导期(OIT) | 100 Min | ASTM D3895 | 200 °C |