ExxonMobil™ LLDPE LL 1002AY Cast
ExxonMobil™ LLDPE LL 1002AY Cast
LLDPE
埃克森美孚化工(ExxonMobil Chemical)
产品描述
LL 1002AY is an LLDPE resin designed for cast films. It offers high gloss and excellent drawdown in both blown and cast film applications. LL 1002AY may also be used as a blend partner with LDPE resins to improve film properties and processability. TnPP is not intentionally added to LL 1002AY resin.
基本信息
| 原厂资料 | 物性表(英文) 物性表(中文) |
| 添加助剂 | 热稳定剂 |
| 成型方式 | 流延薄膜 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 0.918 g/cm³
| ASTM D 1505 | |
熔体质量流动速率(MFR) | | | |
190℃/2.16 kg |
2 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
熔融温度(Tm) | 121 °C
| Internal | Peak |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 1.7 %
| ASTM D1003 | |
光泽度 | 98 -
| ASTM D 2457 | 45° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
7.4 Mpa | ASTM D 882 | MD |
屈服(yld) |
6.5 Mpa | ASTM D 882 | TD |
断裂(brk) |
60 Mpa | ASTM D 882 | MD |
断裂(brk) |
25 Mpa | ASTM D 882 | TD |
拉伸延伸率 | | | |
断裂(brk) |
420 % | ASTM D 882 | MD |
断裂(brk) |
830 % | ASTM D 882 | TD |
穿透强度 | 43 N
| Internal | |
耐穿透性 | 2.3 J
| Internal | |
埃尔曼多夫撕裂 | 20 g
| ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 430 g
| ASTM D 1922 | TD |
割线模量 | 110 Mpa
| ASTM D 882 | 1% Secant, MD |
割线模量 | 130 Mpa
| ASTM D 882 | 1% Secant, TD |
落锤冲击 | 50 g
| ASTM D 1709 | |