ICORENE® N2308
LLDPE
利安德巴塞尔(LyondellBasell)
产品描述
ICORENE® N2308 is a linear low density polyethylene produced by slurry loop low pressure process with hexene as co-monomer.
This grade contains antioxidant stabilizers and has excellent mechanical properties and can be used alone, or blended or co-extruded in a wide variety of blown film applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 易成型抗氧化母粒 | |||
| 添加助剂 | 抗氧化剂 | |||
| 颜色形状 | 粉末状 | |||
| 成型方式 | 流延薄膜吹塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.934 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.15 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 118 °C | ISO 306 | Rate A (50°C/h), Loading 1 (10 N) |
熔融温度(Tm) | 125 °C | ISO 11357-1/-3 | |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 19 Mpa | ISO 527-3 | 0.0200 mm, cast film |
断裂(brk) | 52 Mpa | ISO 527-3 | 0.0200 mm, cast film |
拉伸延伸率 | |||
断裂(brk) | 500 % | ISO 527-3 | 0.0200 mm, cast film |
弯曲模量 | 620 Mpa | ISO 178 | 0.25% Max |