Microthene MP635962
LLDPE
利安德巴塞尔(LyondellBasell)
产品描述
Microthene MP635962 is a high flow hexene LLDPE powder selected by customers for the rotational molding of large hollow objects, including toys, playground equipment, drums and agricultural and chemical storage containers. MP635962 exhibits high ESCR, low temperature impact strength and warp resistance. MP635962 is a UV-stabilized, 35-mesh powder and is also available in pellet form as Petrothene GA635962.
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 产品特性 | 耐低温冲击低翘曲抗紫外线ESCR耐化学性高流动 | |||
| 添加助剂 | 紫外线稳定剂 | |||
| 颜色形状 | 粉末状 | |||
| 成型方式 | 滚塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.935 g/cm3 | ASTM D792 | 23 °C |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 6.7 g/10min | ASTM D1238 | |
环境应力开裂(ESCR ) | 1000 Hours | ASTM D 1693 | F50(100% Igepal?, Cond A) |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 18.6 Mpa | ASTM D638 | |
弯曲模量 | 740 Mpa | ASTM D790 | 1% Secant |
弯曲模量 | 625 Mpa | ASTM D790 | 2% Secant |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
落锤冲击 | 69 J | Internal | -40°C, 3.18 mm |
落锤冲击 | 195 J | Internal | -40°C, 6.35 mm |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm2） | 57 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm2） | 39 °C | ASTM D648 | Unannealed |