Microthene MP625962
LLDPE
利安德巴塞尔(LyondellBasell)
产品描述
Microthene MP625962 is a hexene LLDPE rotational molding powder with excellent flow properties selected by customers to produce a variety of objects such as toys, playground equipment, drums and agricultural and chemical storage containers. MP625962 exhibits high ESCR, low temperature impact strength and warp resistance. MP625962 is a UV-stabilized, 35-mesh powder and is also available in pellet form as Petrothene GA625962.
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 产品特性 | 耐低温冲击低翘曲抗紫外线ESCR耐化学性良好流动性 | |||
| 添加助剂 | 紫外线稳定剂 | |||
| 颜色形状 | 粉末状 | |||
| 成型方式 | 滚塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.935 g/cm3 | ASTM D792 | 23 °C |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 5 g/10min | ASTM D1238 | |
环境应力开裂(ESCR ) | 1000 Hours | ASTM D 1693 | F50(100% Igepal?, Cond A) |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 18.6 Mpa | ASTM D638 | |
弯曲模量 | 725 Mpa | ASTM D790 | 1% Secant |
弯曲模量 | 625 Mpa | ASTM D790 | 2% Secant |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
落锤冲击 | 75 J | Internal | -40°C, 3.18 mm |
落锤冲击 | 210 J | Internal | -40°C, 6.35 mm |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm2） | 55 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm2） | 39 °C | ASTM D648 | Unannealed |