Petrothene NA303013
LDPE
利安德巴塞尔(LyondellBasell)
产品描述
Petrothene NA303 is a series of fractional melt index homopolymer LDPE resins designed for film applications requiring excellent bubble stability/melt strength, impact strength, stiffness and shrink. NA303 is selected by customers for collation shrink films, pallet shrink films, packaging films and heavy duty films where processability, strength and stiffness are important. NA303 contains an antioxidant.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 良好的刚性易成型均聚物 | |||
| 添加助剂 | 抗氧化剂 | |||
| 成型方式 | 吹膜 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.922 g/cm3 | ASTM D 1505 | Base Resin |
密度 | 0.922 g/cm3 | ASTM D 1505 | Product Density |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.25 g/10min | ASTM D1238 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 7.5 % | ASTM D1003 | |
光泽度 | 62 - | ASTM D 2457 | |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 12 Mpa | ASTM D 882 | MD |
屈服(yld) | 12 Mpa | ASTM D 882 | TD |
断裂(brk) | 28 Mpa | ASTM D 882 | MD |
断裂(brk) | 24 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 400 % | ASTM D 882 | MD |
断裂(brk) | 550 % | ASTM D 882 | TD |
埃尔曼多夫撕裂 | 170 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 220 g | ASTM D 1922 | TD |
割线模量 | 220 Mpa | ASTM D 882 | MD, 1% Secant Modulus |
割线模量 | 250 Mpa | ASTM D 882 | TD, 1% Secant Modulus |
落锤冲击 | 190 g | ASTM D 1709 | F50 |