Petrothene NA960000
LDPE
利安德巴塞尔(LyondellBasell)
产品描述
Petrothene NA960 is a series of resins selected by customers for use in a wide variety of industrial film applications where high impact strength and excellent drawdown are needed. NA960 exhibits good uniformity, ease of processing and good tensile strength.
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 产品特性 | 高冲击易成型 | |||
| 成型方式 | 流延薄膜吹塑挤出吹塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.92 g/cm3 | ASTM D 1505 | Base Resin Density, (23 °C) |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 1 g/10min | ASTM D1238 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 14.5 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 990 % | ASTM D638 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 92 °C | ASTM D1525 | |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 11 Mpa | ASTM D 882 | MD |
屈服(yld) | 11 Mpa | ASTM D 882 | TD |
断裂(brk) | 36.5 Mpa | ASTM D 882 | MD |
断裂(brk) | 21.4 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
屈服(yld) | 7 % | ASTM D 882 | MD |
屈服(yld) | 9 % | ASTM D 882 | TD |
断裂(brk) | 120 % | ASTM D 882 | MD |
断裂(brk) | 620 % | ASTM D 882 | TD |
埃尔曼多夫撕裂 | 500 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 100 g | ASTM D 1922 | TD |
割线模量 | 221 Mpa | ASTM D 882 | 1% Secant Modulus, MD |
割线模量 | 297 Mpa | ASTM D 882 | 1% Secant Modulus, TD |
落锤冲击 | 85 g | ASTM D 1709 | F50 |