Petrothene L2560S
LDPE
利安德巴塞尔(LyondellBasell)
产品描述
PETROTHENE L 2560S is a fractional melt index LDPE resin that exhibits a good balance of strength, clarity and heat seal characteristics. L 2560S is formulated without slip but with a medium antiblock level. Typical applications include produce bags, shrink wrap, frozen food containers, bundling and diaper films.
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 产品特性 | 食品接触级 | |||
| 添加助剂 | 开口剂 | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
| 成型方式 | 薄膜挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.925 g/cm3 | ASTM D 1505 | 23 °C |
熔体质量流动速率(MFR) | |||
- | 0.6 g/10min | ASTM D1238 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 8.5 % | ASTM D1003 | 32 μm |
雾度 | 8.5 % | ASTM D1003 | 51 μm |
光泽度 | 60 - | ASTM D 2457 | 45°, 32 μm |
光泽度 | 67 - | ASTM D 2457 | 45°, 51 μm |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 11 Mpa | ASTM D 882 | MD, 32 μm |
屈服(yld) | 11 Mpa | ASTM D 882 | MD, 51 μm |
屈服(yld) | 11.7 Mpa | ASTM D 882 | TD, 32 μm |
屈服(yld) | 11.7 Mpa | ASTM D 882 | TD, 51 μm |
断裂(brk) | 24.1 Mpa | ASTM D 882 | MD, 32 μm |
断裂(brk) | 20 Mpa | ASTM D 882 | MD, 51 μm |
断裂(brk) | 17.2 Mpa | ASTM D 882 | TD, 32 μm |
断裂(brk) | 17.2 Mpa | ASTM D 882 | TD, 51 μm |
拉伸延伸率 | |||
断裂(brk) | 120 % | ASTM D 882 | MD, 32 μm |
断裂(brk) | 230 % | ASTM D 882 | MD, 51 μm |
断裂(brk) | 500 % | ASTM D 882 | TD, 32 μm |
断裂(brk) | 540 % | ASTM D 882 | TD, 51 μm |
埃尔曼多夫撕裂 | 80 g | ASTM D 1922 | MD, 32 μm |
埃尔曼多夫撕裂 | 450 g | ASTM D 1922 | MD, 51 μm |
埃尔曼多夫撕裂 | 80 g | ASTM D 1922 | TD, 32 μm |
埃尔曼多夫撕裂 | 300 g | ASTM D 1922 | TD, 51 μm |
割线模量 | 248 Mpa | ASTM D 882 | 1% Secant, MD, 32 μm |
割线模量 | 228 Mpa | ASTM D 882 | 1% Secant, MD, 51 μm |
割线模量 | 290 Mpa | ASTM D 882 | 1% Secant, TD, 32 μm |
割线模量 | 269 Mpa | ASTM D 882 | 1% Secant, TD, 51 μm |
落锤冲击 | 80 g | ASTM D 1709 | F50, 32 μm |
落锤冲击 | 120 g | ASTM D 1709 | F50, 51 μm |