Petrothene NA952094
LDPE
利安德巴塞尔(LyondellBasell)
产品描述
Petrothene NA952094 is a low density homopolymer resin selected by customers for use in industrial and consumer packaging as well as liner and bag applications. NA952094 has an excellent balance of processability, toughness and drawdown.
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 产品特性 | 易成型均聚物 | |||
| 添加助剂 | 增滑剂开口剂 | |||
| 成型方式 | 流延薄膜吹塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.919 g/cm3 | ASTM D 1505 | Base Resin Density, (23 °C) |
密度 | 0.921 g/cm3 | ASTM D 1505 | Product Density, (23 °C) |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 2 g/10min | ASTM D1238 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 12.4 Mpa | ASTM D 638 | |
拉伸延伸率 | |||
断裂(brk) | 650 % | ASTM D638 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 85 °C | ASTM D1525 | |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 22.1 Mpa | ASTM D 882 | MD |
断裂(brk) | 15.9 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 200 % | ASTM D 882 | MD |
断裂(brk) | 500 % | ASTM D 882 | TD |
埃尔曼多夫撕裂 | 350 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 70 g | ASTM D 1922 | TD |
割线模量 | 183 Mpa | ASTM D 882 | 1% Secant Modulus, MD |
割线模量 | 221 Mpa | ASTM D 882 | 1% Secant Modulus, TD |
落锤冲击 | 110 g | ASTM D 1709 | F50 |