Petrothene NA336149
LDPE
利安德巴塞尔(LyondellBasell)
产品描述
Petrothene NA336149 is a low density homopolymer resin selected by customers for applications that require thin gauge film constructions. NA336149 is known for its consistency, excellent drawdown and processability.
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 产品特性 | 易成型均聚物 | |||
| 添加助剂 | 增滑剂开口剂 | |||
| 成型方式 | 流延薄膜吹塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.92 g/cm3 | ASTM D 1505 | 23 °C |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 6.5 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 85 °C | ASTM D1525 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 8 % | ASTM D1003 | |
光泽度 | 62 - | ASTM D 2457 | 45° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 17.2 Mpa | ASTM D 882 | MD |
断裂(brk) | 13.9 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 225 % | ASTM D 882 | MD |
断裂(brk) | 450 % | ASTM D 882 | TD |
埃尔曼多夫撕裂 | 350 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 150 g | ASTM D 1922 | TD |
割线模量 | 146 Mpa | ASTM D 882 | 1% Secant Modulus, MD |
割线模量 | 165 Mpa | ASTM D 882 | 1% Secant Modulus, TD |
落锤冲击 | 90 g | ASTM D 1709 | F50 |