Petrothene NA334000
LDPE
利安德巴塞尔(LyondellBasell)
产品描述
Petrothene NA334000 is a low density homopolymer resin selected by customers for thin film and profile applications. NA334000 is known for its consistency, exceptional drawdown and processability.
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 产品特性 | 易成型均聚物 | |||
| 成型方式 | 流延薄膜吹塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.919 g/cm3 | ASTM D 1505 | 23 °C |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 6 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 85 °C | ASTM D1525 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 12 % | ASTM D1003 | |
光泽度 | 50 - | ASTM D 2457 | 45° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 15.2 Mpa | ASTM D 882 | MD |
断裂(brk) | 13.8 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 300 % | ASTM D 882 | MD |
断裂(brk) | 450 % | ASTM D 882 | TD |
割线模量 | 138 Mpa | ASTM D 882 | 1% Secant Modulus, MD |
割线模量 | 159 Mpa | ASTM D 882 | 1% Secant Modulus, TD |
落锤冲击 | 65 g | ASTM D 1709 | F50 |