Hostalen CRP 100 BLACK (XL)
HDPE
利安德巴塞尔(LyondellBasell)
产品描述
Hostalen CRP 100 black (XL) is a high density polyethylene (HDPE), black colored similar RAL 9004 with high melt viscosity particularly higher zero viscosity than standard compounds. Typical application: Extrusion of extra large and thick walled pipes to avoid the sagging of the melt and to maintain uniform wall thickness.
The product is classified as PE 100 and provides good stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength.
This grade is not intended for medical and pharmaceutical applications.
This grade is supported for use in drinking water applications.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 耐热老化耐磨抗蠕变易焊接饮用水级抗紫外线耐候性ESCR耐化学性高粘度高熔体强度 | |||
| 颜色形状 | 黑色 | |||
| 成型方式 | 挤出片材挤出管材挤出 | |||
| 增强填充 | 2.25% 炭黑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.959 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
190℃/5 kg | 0.23 g/10 min | ISO 1133 | |
190℃/21.6 kg | 6.4 g/10 min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 23 Mpa | ISO 527-1/-2 | 23 °C, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 8 % | ISO 527-1/-2 | 23 °C, 50 mm/min |
断裂(brk) | 350 % | ISO 527-1/-2 | 23 °C |
拉伸模量 | 1100 Mpa | ISO 527-1/-2 | 23 °C |
拉伸蠕变模量 | |||
1h | 850 Mpa | ISO 899-1 | 2 MPa |
1000h | 360 Mpa | ISO 899-1 | 2 MPa |
弯曲蠕变模量 | 1200 Mpa | DIN 16841 | 4-point loading / 1 min |
弯曲蠕变模量 | 330 Mpa | DIN 16841 | 4-point loading / 2000 hr |
弯曲蠕变模量 | 560 Mpa | DIN 16841 | 4-point loading / 24 hr |
全缺口蠕变试验(FNCT) | 1000 hr | ISO 16770 | 4.0 MPa, 2% Arkopal N100, 80 °C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 13 kJ/m² | ISO 179-1/1eA | |
23℃ (73℉) | 26 kJ/m² | ISO 179-1/1eA | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 63 D | ISO 868 | 3 sec |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 74 °C | ISO 306/B50 | |
熔融温度(Tm) | 129 °C | DSC | |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
氧化诱导期(OIT) | 30 Min | ISO 11357 | 210 °C |
最小环向张应力强度(MRS) | 10 Mpa | ISO 9080 | |
嗅觉阈 | 2 - | EN 1622/EN 1420 | measured on pellets / 30°C / 4 h extraction time |