DOW™ HDPE 05962B
HDPE
陶氏化学(Dow Chemical)
产品描述
DOW HDPE 05962B is a High Density Polyethylene produced via SOLUTION™ technology. This resin presents a narrow molecular weight distribution that offers excellent impact resistance in rigid packaging, high gloss, excellent stiffness and processability.
Main Characteristics
Resin for Injection Molding
Pails and Crates
Resin for Cast film
Film for diapers, femine hygiene
Complies with:
U.S. FDA 21 CFR 177.1520 (c) 3.1a
EU, No 10/2011
Consult the regulations for complete details
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 法规认证 | EU Food Contact(2011/10/EC)(欧盟食品级)FDA(食品药品监督管理局) | |||
| 成型方式 | 注塑薄膜挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.958 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 5 g/10min | ASTM D1238 | |
环境应力开裂(ESCR ) | 44 Hours | ASTM D 1693 | Compression Molded |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 29 Mpa | ASTM D638 | Compression Molded |
断裂(brk) | 25 Mpa | ASTM D638 | Compression Molded |
拉伸延伸率 | |||
断裂(brk) | 2400 % | ASTM D638 | Compression Molded |
弯曲模量 | 110 Mpa | ASTM D790 | Compression Molded |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
- | 25 J/m | ASTM D 256 | Compression Molded |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 82 D | ASTM D 2240 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
加工温度 | 268 °C | - | Extrusion |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 6 % | ASTM D1003 | 24 µm |
光泽度 | 85 - | ASTM D 2457 | 45°, 24 µm |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 27 Mpa | ASTM D 882 | MD, 24 µm |
屈服(yld) | 28 Mpa | ASTM D 882 | TD, 24 µm |
断裂(brk) | 36 Mpa | ASTM D 882 | MD, 24 µm |
断裂(brk) | 28 Mpa | ASTM D 882 | TD, 24 µm |
拉伸延伸率 | |||
断裂(brk) | 600 % | ASTM D 882 | MD, 24 µm |
断裂(brk) | 650 % | ASTM D 882 | TD, 24 µm |
耐穿透性 | 3.31 J/cm³ | Internal | 24 µm |
埃尔曼多夫撕裂 | 40 g | ASTM D 1922 | MD, 24 µm |
埃尔曼多夫撕裂 | 120 g | ASTM D 1922 | TD, 24 µm |
割线模量 | 472 Mpa | ASTM D 882 | 2% Secant, MD, 24 µm |
割线模量 | 672 Mpa | ASTM D 882 | 2% Secant, TD, 24 µm |
落锤冲击 | 8 g | ASTM D 1709 | 24 µm |