Borstar® HE6067
HDPE
博禄/北欧化工(Borealis AG/Borouge)
产品描述
Borstar HE6067 is a black high density (HD) jacketing compound, which is produced with the Borealis proprietary Borstar bimodal process technology.
Borstar technology allows the manufacturing of polymers outside the traditional MFR and density range making it possible to optimize processability, reduce shrinkage and yet provide excellent physical toughness and environmental stress crack resistance (ESCR).
Borstar HE6067 contains 2.5% well-dispersed carbon black in order to ensure excellent weathering resistance.
Applications
Borstar HE6067 is designed for jacketing of energy and communication cables.
Borstar HE6067 offers substantially reduced shrinkage which helps to maintain low signal attenuation for fibre optic communication cables and low jacket retraction for energy cables in combination with excellent mechanical and barrier properties. Borstar HE6067 offers a balance of properties giving advantages in manufacturing, installation and lifetime performance of communication and energy cables.
Specifications
Borstar HE6067 meets the applicable requirements as below when processed using sound extrusion practice and testing procedure: ASTM D 1248 Type III, Class C, Category 3, Grade J4, E8, E9, W8 ISO 1872-PE, KCHL, 40 D-022
The following cable material standards are met by Borstar HE6067: DIN VDE 0207 Type 2YM3 EN 50290-2-24 DMP 2, 5, 7, 8, 9, 10, 11, 12, 14, 15
Cables manufactured with Borstar HE6067 using sound extrusion practice normally comply with the following cable product standards: IEC 60502, Part 2, Type ST7 IEC 60708 IEC 60840, Type ST7 IEC 60794 EN 187105 DIN VDE 0818 HD 603 S1, DMP 1, 2, 5, 7, 8 HD 620 S2, Part 1, table 4B, DMP 2, 8-12, 14-15, 17 HD 632 S2, ST7
Special Features
Borstar HE6067 consists of specially selected components to offer: Superior processability Excellent environmental stress cracking resistance (ESCR) Good abrasion & scratch resistance Low water permeability Low heat deformation Good petroleum-jelly resistance
基本信息
原厂资料 | 物性表-ISO(英文) | |||
产品特性 | 耐磨耐刮擦易成型耐候性ESCR | |||
颜色形状 | 黑色 | |||
成型方式 | 线缆挤出 | |||
增强填充 | 2.5% 炭黑 |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 0.942 g/cm³ | ISO 1183 | Base Resin |
密度 | 0.954 g/cm³ | ISO 1183 | Compound |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 1.7 g/10min | ISO 1133 | |
环境应力开裂(ESCR ) | 5000 Hours | IEC 60811-406 | 50 °C, Igepal 10 %, F0 |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 29 Mpa | ISO 527-2 | 50 mm/min |
拉伸延伸率 | |||
断裂(brk) | 900 % | ISO 527-2 | 50 mm/min |
弯曲模量 | 900 Mpa | ISO 178 | |
冲击性能 | 值/单位 | 测试标准 | 测试条件 |
脆化温度 | -76 °C | ASTM D 746 | |
硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 61 D | ISO 868 | 1 s |
电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+16 Ohm-cm | IEC 60093 | |
绝缘强度 | 20 kV/mm | IEC 60243 | |
光学性能 | 值/单位 | 测试标准 | 测试条件 |
吸光系数 | 400 - | ASTM D3349 | abs/m |