| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 0.94 g/cm³
| ASTM D 1505 | |
熔体质量流动速率(MFR) | | | |
190℃/2.16 kg |
2 g/10min | ASTM D1238 | |
环境应力开裂(ESCR ) | 40 Hours
| ASTM D 1693 | 10% Igepal, Compression Molded, F50 |
环境应力开裂(ESCR ) | 560 Hours
| ASTM D 1693 | 100% Igepal, Compression Molded, F50 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
19.3 Mpa | ASTM D638 | 51 mm/min, Rotational Molded |
拉伸延伸率 | | | |
断裂(brk) |
10 % | ASTM D638 | Rotational Molded |
弯曲模量 | 896 Mpa
| ASTM D790 | 1% Secant, Rotational Molded |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
落锤冲击 | 88 J
| Internal | -40°C, 3.18 mm, Rotational Molded |
落锤冲击 | 258 J
| Internal | -40°C, 6.35 mm, Rotational Molded |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
57.2 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
37.8 °C | ASTM D648 | Unannealed |
熔融温度(Tm) | 129 °C
| ASTM D3418 | Peak Melting Temperature |