Hostalen ACP 6031D
HDPE
利安德巴塞尔(LyondellBasell)
产品描述
Hostalen ACP 6031D is a high density polyethylene resin used in small blow molding applications such as thinwall packaging and consumer goods. It exhibits very high stiffness. Hostalen ACP 6031D is delivered in pellet form, contains antioxidants and has a broad molecular weight distribution.
Hostalen ACP 6031D is not intended for use in medical and pharmaceutical applications.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高刚性抗氧化ESCR | |||
| 添加助剂 | 抗氧化剂 | |||
| 成型方式 | 吹塑注塑吹塑挤出吹塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.96 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.35 g/10min | ISO 1133 | |
190℃/5 kg | 1.2 g/10 min | ISO 1133 | |
190℃/21.6 kg | 23 g/10 min | ISO 1133 | |
堆积(视)密度 | 0.5 g/cm³ | ISO 60 | |
环境应力开裂(ESCR ) | 130 Hours | ASTM D 1693 | F50, Cond. B, 10% Arkopal N100 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 30 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
屈服(yld) | 7 % | ISO 527-1/-2 | |
拉伸模量 | 1420 Mpa | ISO 527-1/-2 | |
全缺口蠕变试验(FNCT) | 7 hr | ISO 16770 | 3.5 MPa, 2% Arkopal N100, 80 °C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 6 kJ/m² | ISO 179 | Type 1, Edgewise, Notch A |
拉伸冲击 | 65 kJ/m² | ISO 8256 | notched, -30°C |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 64 D | ISO 868 | |
球压硬度 | 63 Mpa | ISO 2039-1 | H 132/30 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
熔融温度(Tm) | 180~210 °C | Internal |