Marlex® 9608XD
HDPE
雪佛龙菲利普斯(Chevron Phillips)
产品描述
This high density polyethylene is tailored for cast film applications that require:
• Very low gel levels
• Very "clear" film
• Excellent drawdown
• Enhanced stiffness
• Excellent WVTR for a chill cast film
• Excellent processability
Typical cast film applications include:
• Coextrusions
• Overwrap
• Food packaging
• Moisture sensitive packaging
This high density polyethylene can also be used in extrusion coating applications that require:
• Enhanced stiffness
• Abrasion resistance
• Increased temperature resistance
• Improved WVTR
This high density grade is designed to be blended or coextruded with a low density polyethylene (LDPE) coating grade, if used in extrusion coating. Please contact your Technical Service representative for further information regarding blending this resin with LDPE.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 成型方式 | 流延薄膜 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.962 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 8 g/10min | ASTM D1238 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 11 % | ASTM D1003 | 1.25 mil Blown Film |
光泽度 | 120 - | ASTM D 2457 | 60°, 1.25 mil Blown Film |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 29 Mpa | ASTM D 882 | MD, 1.25 mil Blown Film |
断裂(brk) | 23 Mpa | ASTM D 882 | TD, 1.25 mil Blown Film |
拉伸延伸率 | |||
断裂(brk) | 870 % | ASTM D 882 | MD, 1.25 mil Blown Film |
断裂(brk) | 790 % | ASTM D 882 | TD, 1.25 mil Blown Film |
埃尔曼多夫撕裂 | 35 g/mil | ASTM D 1922 | MD, 1.25 mil Blown Film |
埃尔曼多夫撕裂 | 100 g/mil | ASTM D 1922 | TD, 1.25 mil Blown Film |
割线模量 | 758 Mpa | ASTM D 882 | 1 % Secant, MD, 1.25 mil Blown Film |
割线模量 | 841 Mpa | ASTM D 882 | 1 % Secant, TD, 1.25 mil Blown Film |
落锤冲击 | 35 g/mil | ASTM D 1709 | 1.25 mil Blown Film |
水蒸气渗透系数 | 5 g/m²/24 hr | ASTM F 1249 | 1.25 mil Blown Film |