PRE-ELEC® PE 1294
HDPE
普宓斯(PREMIX)
产品描述
PRE-ELEC® PE 1294 is a conductive thermoplastic compound based on PE-HD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PE 1294 has an excellent balance of mechanical properties and is easy to injection mould.
Typical applications include large plastic parts like pallets, drums and containers.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 导电 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 炭黑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.01 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 2 g/10min | ISO 1133 | |
190℃/10 kg | 20 g/10 min | ISO 1133 | |
190℃/21.6 kg | 80 g/10 min | ISO 1133 | |
收缩率 | |||
- | 1.5~2.5 % | ISO 294-4 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 23 Mpa | ISO 527 | |
- | 12 Mpa | ISO 527 | |
拉伸延伸率 | |||
屈服(yld) | 15 % | ISO 527 | |
断裂(brk) | 300 % | ISO 527 | |
弯曲模量 | 1000 Mpa | ISO 178 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-20℃ (-4℉) | 10 kJ/m² | ISO 179 | 4.0 mm |
23℃ (73℉) | 15 kJ/m² | ISO 179 | 4.0 mm |
简支梁无缺口(Charpy Unnotched) | |||
-20℃ (-4℉) | NB kJ/m² | ISO 179 | 4.0 mm |
23℃ (73℉) | NB kJ/m² | ISO 179 | 4.0 mm |
悬臂梁缺口(Izod Notched) | |||
-20℃ (-4℉) | 4 kJ/m² | ISO 180 | 4.0 mm |
23℃ (73℉) | 12 kJ/m² | ISO 180 | 4.0 mm |
悬臂梁无缺口(Izod Unnotched) | |||
-20℃ (-4℉) | NB kJ/m² | ISO 180 | 4.0 mm |
23℃ (73℉) | NB kJ/m² | ISO 180 | 4.0 mm |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 A | 95 A | ISO 868 | |
邵氏硬度 D | 66 D | ISO 868 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 76 °C | ISO 75/Bf | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 45 °C | ISO 75/Af | |
维卡软化温度(Vicat) | 63 °C | ISO 306/B50 | |
维卡软化温度(Vicat) | 125 °C | ISO 306/A50 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1E+4 Ohm-cm | Internal | |
表面电阻率 | 1E+5 Ohm | IEC 61340-2-3 |