ICORENE® N2808
HDPE
利安德巴塞尔(LyondellBasell)
产品描述
ICORENE® N2808 is a gas phase homopolymer HDPE and offers high stiffness, high temperature resistance (antioxidant stabilizers), low water vapour transmission and relatively high grease resistance.
This grade has a low gel level. It's typically used for masterbatch applications related to food packaging, release paper and photographic paper.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高刚性耐热易成型抗氧化 | |||
| 添加助剂 | 抗氧化剂 | |||
| 法规认证 | EU Food Contact(2011/10/EC)(欧盟食品级)FDA(食品药品监督管理局) | |||
| 颜色形状 | 粉末状 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.963 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 8 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
熔融温度(Tm) | 134 °C | DIN 53765 | |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 26 Mpa | ISO 527-3 | MD |
屈服(yld) | 24 Mpa | ISO 527-3 | TD |
断裂(brk) | 22 Mpa | ISO 527-3 | MD |
断裂(brk) | 18 Mpa | ISO 527-3 | TD |
拉伸延伸率 | |||
断裂(brk) | 700 % | ISO 527-3 | MD |
断裂(brk) | 800 % | ISO 527-3 | TD |
水蒸气渗透系数 | 4 g/m²/24 hr | Internal | 38°C at 100% RH |
氧渗透 | 0.1 cm³·mm/m²/atm/24 hr | Internal | 23°C |
弯曲模量 | 580 Mpa | ISO 178 | MD |
弯曲模量 | 580 Mpa | ISO 178 | TD |