Marlex® HMN 6060UV
HDPE
雪佛龙菲利普斯(Chevron Phillips)
产品描述
This high density polyethylene is an ethylene-hexene copolymer tailored for injection molding applications that require:
• Excellent stiffness
• Strong UV resistance
• Good impact strength
• Durability
• Moderate flow
Typical injection molding applications for HMN 6060UV include:
• Crates
• Tote boxes
• Structural foam (with proper foaming agent)
This resin meets these specifications:
• ASTM D4976 – PE 233
• FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per 21 CFR 176.170(c)
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 良好的刚性高耐久性良好冲击性可发泡抗紫外线良好流动性 | |||
| 法规认证 | ASTM D4976(聚乙烯注塑和挤压材料标准)FDA(食品药品监督管理局) | |||
| 成型方式 | 注塑发泡 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.962 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 6.5 g/10min | ASTM D1238 | |
环境应力开裂(ESCR ) | 15 Hours | ASTM D 1693 | Condition B (100 % Igepal), F50 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 32 Mpa | ASTM D638 | Tangent - 16:1 span:depth, 0.5 in/min |
拉伸延伸率 | |||
屈服(yld) | 8 % | ASTM D638 | 2 in/min, Type IV bar/min |
断裂(brk) | 900 % | ASTM D638 | 2 in/min, Type IV bar |
弯曲模量 | 1586 Mpa | ASTM D790 | 1 % Secant, 16:1 span:depth, 0.5 in/min |
弯曲模量 | 1758 Mpa | ASTM D790 | Tangent, 16:1 span:depth, 0.5 in/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 35 J/m | ASTM D256 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 20 J | ASTM D3763 | 21.6 ft/sec, 73.4 °F, 0.125 in |
23℃ (73℉)总能量 | 31 J | ASTM D3763 | 21.6 ft/sec, 73.4 °F, 0.125 in |
脆化温度 | -75 °F | ASTM D 746 | Type A, Type I specimen |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 66 D | ASTM D 2240 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 87 °C | ASTM D648 | Method A |
1.8 Mpa (264 psi)（18.6kg/cm²） | 51 °C | ASTM D648 | Method A |
维卡软化温度(Vicat) | 127 °C | ASTM D1525 | Loading 1, Rate A |