SABIC® HDPE PCGF0863
HDPE
沙特基础 (SABIC)
产品描述
SABIC® HDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity.
SABIC® HDPE PCGF0863 resin is a high density homopolymer with good barrier properties. The grade offers high stiffness, high temperature resistance and relatively high grease resistance. The resin has a low gel level.
SABIC® HDPE PCGF0863 is typically used for flexible packaging, pharmaceuticals and devices and release liners.
Film properties have been measured at cast film of 25 µm. Water vapor permeability at 38 °C and 100 % RH per 24 h. Oxygen permeability at 23 °C and 0 % RH per 24 h.
Compliance to regulations.
SABIC® HDPE PCGF0863 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI).
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高刚性耐热医疗级耐油均聚物高阻隔性 | |||
| 法规认证 | EP(欧洲药典)USP Class VI(美国药典) | |||
| 成型方式 | 薄膜挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.964 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 8 g/10min | ISO 1133 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
熔融温度(Tm) | 134 °C | DIN 53765 | |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 26 Mpa | ISO 527-3 | MD |
屈服(yld) | 24 Mpa | ISO 527-3 | TD |
断裂(brk) | 22 Mpa | ISO 527-3 | MD |
断裂(brk) | 18 Mpa | ISO 527-3 | TD |
拉伸延伸率 | |||
断裂(brk) | 700 % | ISO 527-3 | MD |
断裂(brk) | 800 % | ISO 527-3 | TD |
水蒸气渗透系数 | 4 g/m²/24 hr | Internal | |
氧渗透 | 0.1 ml/m2 day | Internal | |
弹性模量 | 580 MPa | ISO 527-3 | MD |
弹性模量 | 580 MPa | ISO 527-3 | TD |