Marlex® 9010C
HDPE
雪佛龙菲利普斯(Chevron Phillips)
产品描述
This high density polyethylene is an ethylene-hexene copolymer tailored for injection molded applications that require:
• Good flow performance
• Slip agent with good organoleptics and high oxidative stability
• High impact strength
• Excellent stiffness
Typical injection molded applications for 9010C include items such as:
• Caps
• Closures
• Containers
This resin meets these specifications:
• ASTM D4976 - PE 233
• FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per 21 CFR 176.170(c)
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 良好的刚性高冲击抗氧化良好流动性 | |||
| 添加助剂 | 增滑剂 | |||
| 法规认证 | ASTM D4976(聚乙烯注塑和挤压材料标准)FDA(食品药品监督管理局) | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.945 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 10 g/10min | ASTM D1238 | |
环境应力开裂(ESCR ) | 20 Hours | ASTM D 1693 | Condition B (10 % Igepal), F50 |
环境应力开裂(ESCR ) | 49 Hours | ASTM D 1693 | Condition B (100 % Igepal), F50 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 21 Mpa | ASTM D638 | 2 in/min, Type IV bar |
拉伸延伸率 | |||
断裂(brk) | 500 % | ASTM D638 | 2 in/min, Type IV bar |
弯曲模量 | 950 Mpa | ASTM D790 | 1 % Secant, 16:1 span:depth, 0.5 in/min |
弯曲模量 | 1010 Mpa | ASTM D790 | Tangent - 16:1 span:depth, 0.5 in/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 59 J/m | ASTM D256 | |
脆化温度 | -75 °C | ASTM D 746 | Type A, Type I specimen |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 60 D | ASTM D 2240 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 67 °C | ASTM D648 | Method A |
1.8 Mpa (264 psi)（18.6kg/cm²） | 44 °C | ASTM D648 | Method A |
维卡软化温度(Vicat) | 114 °C | ASTM D1525 | Loading 1, Rate A |