Marlex® 9514H
HDPE
雪佛龙菲利普斯(Chevron Phillips)
产品描述
This gas phase, high molecular weight, ethylene-hexene copolymer is tailored for lightweight blow molded applications that require:
• Excellent balance of stiffness and ESCR
• Good melt strength
• Durability
Typical blow molded applications for 9514H include:
• Household and industrial chemical containers
• Large parts
This resin meets these specifications:
• ASTM D4976 - PE 235
• FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per Table 2 of 21 CFR 176.170(c)
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高耐久性ESCR高熔体强度 | |||
| 法规认证 | ASTM D4976(聚乙烯注塑和挤压材料标准)FDA(食品药品监督管理局) | |||
| 成型方式 | 吹塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.957 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.3 g/10min | ASTM D1238 | |
环境应力开裂(ESCR ) | 50 Hours | ASTM D 1693 | Condition B (100 % Igepal), F50 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 30 Mpa | ASTM D638 | 2 in/min, Type IV bar |
拉伸延伸率 | |||
断裂(brk) | 800 % | ASTM D638 | 2 in/min, Type IV bar |
弯曲模量 | 1410 Mpa | ASTM D790 | Tangent - 16:1 span:depth, 0.5 in/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
脆化温度 | -75 °C | ASTM D 746 | Type A, Type I specimen |