SABIC® HDPE FJ00952
HDPE
沙特基础 (SABIC)
产品描述
FJ00952 is TNPP additive free grade, high molecular weight High Density Polyethylene copolymer which has a broad molecular weight distribution. The design of the product, molecular architecture and density, gives it a unique combination of easy extrusion and high melt strength with strong physical properties which makes it suitable for producing thin films with excellent strength and rigidity.
TYPICAL APPLICATIONS
FJ00952 resin is recommended for blown film extrusion. This product is suggested for the manufacture of high strength grocery sacks, shopping bags and high quality thin films for multi wall sack liners and replacement for thin paper products. Films of this product can be readily treated and printed to give high quality graphics.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 成型方式 | 挤出吹膜 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.952 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.05 g/10min | ASTM D1238 | |
190℃/21.6 kg | 9 g/10 min | ASTM D 1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 125 °C | ASTM D1525 | |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 33 Mpa | ASTM D 882 | MD, 15 μm film |
屈服(yld) | 31 Mpa | ASTM D 882 | TD, 15 μm film |
断裂(brk) | 60 Mpa | ASTM D 882 | MD, 15 μm film |
断裂(brk) | 56 Mpa | ASTM D 882 | TD, 15 μm film |
拉伸延伸率 | |||
断裂(brk) | 400 % | ASTM D 882 | MD, 15 μm film |
断裂(brk) | 550 % | ASTM D 882 | TD, 15 μm film |
埃尔曼多夫撕裂 | 12 g | ASTM D 1922 | MD, 15 μm film |
埃尔曼多夫撕裂 | 60 g | ASTM D 1922 | TD, 15 μm film |
割线模量 | 1250 Mpa | ASTM D 882 | MD, 15 μm film, 1% secant |
割线模量 | 1500 Mpa | ASTM D 882 | TD, 15 μm film, 1% secant |
落锤冲击 | 180 g/µm | ASTM D 1709 | 15 μm film |