DOW™ HDPE DGDA-5004 NT 7
HDPE
陶氏化学(Dow Chemical)
产品描述
DOW DGDA-5004 NT 7 High Density Polyethylene (HDPE) resin is a multi-purpose polymer designed for sheet extrusion and thermoforming applications, including single-serve disposables and other thin walled containers.
Main Characteristics:
Maximum rigidity
High Impact Strength
Good Top Load Strength
Optimized Shear Rheology for Good Processability
Complies with U.S. FDA 21 CFR 177.1520 (c) 2.2
Consult the regulations for complete details.
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
| 成型方式 | 挤出片材挤出热成型 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.961 g/cm³ | ASTM D792 | |
密度 | 0.961 g/cm³ | Internal | Base Density |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.8 g/10min | ASTM D1238 | |
190℃/21.6 kg | 57 g/10 min | ASTM D 1238 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 31.7 Mpa | ASTM D638 | |
断裂(brk) | 24.1 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 7 % | ASTM D638 | |
断裂(brk) | 1000 % | ASTM D638 | |
弯曲模量 | 1300 Mpa | ASTM D790 | 2% Secant |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸冲击 | 84.1 kJ/m² | ASTM D 1822 | Type S |
脆化温度 | -76.1 °C | ASTM D 746 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 66 D | ASTM D 2240 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 76.1 °C | ASTM D648 | Unannealed |
维卡软化温度(Vicat) | 131 °C | ASTM D1525 | |
熔融温度(Tm) | 133 °C | Internal | DSC |
结晶温度 | 120 °C | Internal | DSC |