SABIC® HDPE F00952J
HDPE
沙特基础 (SABIC)
产品描述
SABIC® HDPE F00952J resin is a high molecular weight, TNPP free high density polyethylene copolymer. The design of the product, molecular architecture and density, gives F00952J a good combination of easy extrusion and high melt strength with strong physical properties. Typical applications are thin films with excellent strength and rigidity.
The material contains anti-oxidants.
SABIC® HDPE F00952J resin is typically used for blown film extrusion and production of high strength grocery sacks, shopping bags and high quality thin films for multi wall sack liners and replacement for thin paper products.
SABIC® HDPE F00952J can be extruded on conventional HMW-HDPE equipment at melt temperature settings between 200 and 220 °C.
Film properties have been measured at 15 µm blown film with a BUR = 4.
This product is not intended for and must not be used in any pharmaceutical/medical applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 添加助剂 | 抗氧化剂 | |||
| 成型方式 | 挤出吹膜 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.952 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.05 g/10min | ISO 1133 | |
190℃/21.6 kg | 9.5 g/10 min | ISO 1133 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 125 °C | ASTM D1525 | |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 33 Mpa | ASTM D 882 | MD |
屈服(yld) | 40 Mpa | ASTM D 882 | TD |
断裂(brk) | 66 Mpa | ASTM D 882 | MD |
断裂(brk) | 64 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 400 % | ASTM D 882 | MD |
断裂(brk) | 550 % | ASTM D 882 | TD |
埃尔曼多夫撕裂 | 12 g/µm | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 60 g/µm | ASTM D 1922 | TD |
落锤冲击 | 180 g | ASTM D 1709 | F50, 15 µm film |
弹性模量 | 1250 MPa | ASTM D882 | MD |
弹性模量 | 1500 MPa | ASTM D882 | TD |