Hostalen CRP 100 RESIST CR BLACK
HDPE
利安德巴塞尔(LyondellBasell)
产品描述
Hostalen CRP 100 RESIST CR black is a high density polyethylene (HDPE), black coloured similar RAL 9004 with high melt viscosity for extrusion, injection and compression moulding. The product is classified as PE 100- RC and provides a very good long term hydrostatic strength. Especially developed for non-conventional pipe installation methods the product has a superior resistance to slow crack growth. It fulfils the material requirements of PAS 1075:2009-04.
This grade is not intended for medical and pharmaceutical applications.
This grade is supported for use in drinking water applications.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 耐热老化耐磨抗蠕变易焊接饮用水级抗紫外线耐候性ESCR耐化学性高粘度 | |||
| 法规认证 | PAS 1075:2009-04(聚乙烯管材) | |||
| 颜色形状 | 黑色 | |||
| 成型方式 | 注塑挤出模压 | |||
| 增强填充 | 2.25% 炭黑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.958 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
190℃/5 kg | 0.23 g/10 min | ISO 1133 | |
190℃/21.6 kg | 6.4 g/10 min | ISO 1133 | |
堆积(视)密度 | 0.58 g/cm³ | ISO 60 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 23 Mpa | ISO 527-1/-2 | 23 °C, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 9 % | ISO 527-1/-2 | 23 °C, 50 mm/min |
断裂(brk) | 350 % | ISO 527-1/-2 | 23 °C |
拉伸模量 | 1100 Mpa | ISO 527-1/-2 | 23 °C |
拉伸蠕变模量 | |||
1h | 850 Mpa | ISO 899-1 | 2 MPa |
1000h | 360 Mpa | ISO 899-1 | 2 MPa |
弯曲蠕变模量 | 1200 Mpa | DIN 16841 | 4-point loading / 1 min |
弯曲蠕变模量 | 330 Mpa | DIN 16841 | 4-point loading / 2000 hr |
弯曲蠕变模量 | 560 Mpa | DIN 16841 | 4-point loading / 24 hr |
全缺口蠕变试验(FNCT) | 8760 hr | ISO 16770 | 4.0 MPa, 2% Arkopal N100, 80 °C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 13 kJ/m² | ISO 179-1/1eA | |
23℃ (73℉) | 26 kJ/m² | ISO 179-1/1eA | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 63 D | ISO 868 | 3 sec |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 74 °C | ISO 306/B50 | |
熔融温度(Tm) | 129 °C | DSC | |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
氧化诱导期(OIT) | 30 Min | ISO 11357 | 210 °C |
最小环向张应力强度(MRS) | 10 Mpa | ISO 9080 | |
嗅觉阈 | 2 - | EN 1622/EN 1420 | measured on pellets / 30°C / 4 h extraction time |