Hostalen CRP 100 RESIST CR orange
HDPE
利安德巴塞尔(LyondellBasell)
产品描述
Hostalen CRP 100 RESIST CR orange is a high density polyethylene (HDPE), orange colored similar RAL 1033 with high melt viscosity for extrusion, injection and compression molding. The compound fulfills the material requirements of EN 1555-1 and ISO 4437-1. The product is additionally classified as PE 100-RC and provides a very good long term hydrostatic strength. Especially developed for non-conventional pipe installations methods the product has a superior resistance to slow crack growth.
It fulfills the material requirements of PAS 1075:2009-04.
Designation according ISO 1872-1: PE,EACHL,50-T003
This grade is not intended for medical, pharmaceutical, food and drinking water applications.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | ESCR | |||
| 法规认证 | EN 1555-1(燃气输送塑料管道)ISO 4437-1(燃气埋地聚乙烯(PE)管道)PAS 1075:2009-04(聚乙烯管材) | |||
| 颜色形状 | 橙色 | |||
| 成型方式 | 注塑挤出模压 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.95 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
190℃/5 kg | 0.27 g/10 min | ISO 1133 | |
190℃/21.6 kg | 7.3 g/10 min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 23 Mpa | ISO 527-1/-2 | 23 °C, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 9 % | ISO 527-1/-2 | 23 °C, 50 mm/min |
断裂(brk) | 350 % | ISO 527-1/-2 | 23 °C |
拉伸模量 | 1050 Mpa | ISO 527-1/-2 | 23 °C |
拉伸蠕变模量 | |||
1h | 850 Mpa | ISO 899-1 | 2 MPa |
1000h | 360 Mpa | ISO 899-1 | 2 MPa |
弯曲蠕变模量 | 1100 Mpa | DIN 16841 | 4-point loading / 1 min |
弯曲蠕变模量 | 330 Mpa | DIN 16841 | 4-point loading / 2000 hr |
弯曲蠕变模量 | 560 Mpa | DIN 16841 | 4-point loading / 24 hr |
全缺口蠕变试验(FNCT) | 8760 hr | ISO 16770 | 4.0 MPa, 2% Arkopal N100, 80 °C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 13 kJ/m² | ISO 179-1/1eA | |
23℃ (73℉) | 26 kJ/m² | ISO 179-1/1eA | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 62 D | ISO 868 | 3 sec |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 74 °C | ISO 306/B50 | |
熔融温度(Tm) | 129 °C | DSC | |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
氧化诱导期(OIT) | 30 Min | ISO 11357 | 210 °C |
最小环向张应力强度(MRS) | 10 Mpa | ISO 9080 |