Alathon 9307TC
HDPE
利安德巴塞尔(LyondellBasell)
产品描述
Alathon 9307TC is a bimodal, high molecular weight, high density polyethylene resin with excellent processing characteristics. 9307TC is selected by customers for demanding conduit and corrugated pipe applications.
ASTM D3350 Cell Classification: PE445560
基本信息
| 原厂资料 | 物性表(英文) | |||
| 成型方式 | 挤出管材挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.949 g/cm³ | ASTM D 1505 | 23 °C |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.07 g/10min | ASTM D1238 | |
190℃/21.6 kg | 16 g/10 min | ASTM D 1238 | |
环境应力开裂(ESCR ) | 1000 Hours | ASTM D 1693 | F50(10% Igepal®, Cond B) |
环境应力开裂(ESCR ) | 1000 Hours | ASTM D 1693 | F50(100% Igepal®, Cond B) |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 24.5 Mpa | ASTM D638 | |
断裂(brk) | 34.3 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 600 % | ASTM D638 | |
弯曲模量 | 972 Mpa | ASTM D790 | 2% Secant |
管材缺口拉伸实验 | 100 hr | ASTM F1473 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 68 °C | ASTM D648 | Unannealed |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
氧化诱导期(OIT) | 100 Min | ASTM D3895 | 200 °C |
诱导温度 | 260 °C | ASTM D3350 | |
凹口恒定带状应力试验(NCLS) | 4000 hrs | ASTM F2136 |