SABIC® VESTOLEN A RELY 5922R 10000 BLACK
HDPE
沙特基础 (SABIC)
产品描述
SABIC® Vestolen A RELY 5922R 10000 is a grade which has a high density and a bimodal distribution of the molecular mass. Due to its resistance against slow crack growth (SCG) the material SABIC® Vestolen A RELY 5922R 10000 is considered as PE100-RC and may be used for no dig applications.
Moreover it may be used for the production of thick walled (large diameter and low SDR) pipes for infrastructure and industrial application due to its low sagging characteristics and it shows favorable processing behavior.
This material meets (inter)national standards for use in gas, drinking water and waste water piping.MRS class ISO 12162 MPa = 10.0 (PE 100).
This product is not intended for and must not be used in any pharmaceutical/medical applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 饮用水级 | |||
| 颜色形状 | 黑色 | |||
| 增强填充 | 2.25% 炭黑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.959 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
190℃/5 kg | 0.2 g/10 min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 24 Mpa | ISO 527-2 | 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 9 % | ISO 527-2 | 50 mm/min |
拉伸模量 | 1100 Mpa | ISO 527-2 | 50 mm/min |
全缺口蠕变试验(FNCT) | 8760 hr | ISO 16770 | 2% Arkopal N100 at 80 °C, 4 MPa |
耐裂纹扩展 | 8760 hr | ISO 13479 | |
应变硬化 | 50 Mpa | Internal | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 10 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 26 kJ/m² | ISO 179/1eA | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 62 D | ISO 868 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 72 °C | ISO 75-2/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 45 °C | ISO 75-2/A | |
维卡软化温度(Vicat) | 72 °C | ISO 306/B50 | |
熔融温度(Tm) | 124~128 °C | DIN 53765 | DSC |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
氧化诱导期(OIT) | 20 Min | ISO 11357 | 210 °C |
最小环向张应力强度(MRS) | 10 MPa | ISO 12162 |