Marlex® HXB TR-512
HDPE
雪佛龙菲利普斯(Chevron Phillips)
产品描述
This broad distribution, extra high molecular weight ethylene-hexene copolymer is tailored for large containers that require:
• Outstanding impact resistance
• Outstanding creep resistance
• Excellent ESCR
• Excellent chemical resistance
• Durability
Typical blow molded applications for HXB TR-512 include:
• 55-gallon drums
• Industrial tanks
This resin meets these specifications:
• ASTM D4976 - PE 235
• FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per Table 2 of 21 CFR 176.170(c)
• Listed in the Drug Master File
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高耐久性良好冲击性抗蠕变ESCR耐化学性 | |||
| 法规认证 | ASTM D4976(聚乙烯注塑和挤压材料标准)DMF(药品主控文件)FDA(食品药品监督管理局) | |||
| 成型方式 | 吹塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.954 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 5.5 g/10min | ASTM D1238 | |
环境应力开裂(ESCR ) | 1000 Hours | ASTM D 1693 | Condition B (100 % Igepal), F50 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 29 Mpa | ASTM D638 | 2 in/min, Type IV bar |
拉伸延伸率 | |||
断裂(brk) | 800 % | ASTM D638 | 2 in/min, Type IV bar |
弯曲模量 | 1340 Mpa | ASTM D790 | Tangent - 16:1 span:depth, 0.5 in/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸冲击 | 450 kJ/m² | ASTM D 1822 | Type S bar |
脆化温度 | -75 °C | ASTM D 746 | Type A, Type I specimen |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 60 D | ASTM D 2240 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 74 °C | ASTM D648 | Method A |
维卡软化温度(Vicat) | 126 °C | ASTM D1525 | Loading 1, Rate A |