SABIC® HDPE F00950
HDPE
沙特基础 (SABIC)
产品描述
SABIC® HDPE F00950 resin is a high molecular weight, high density polyethylene copolymer. The design of the product, molecular architecture and density, gives F00950 a good balance of easy extrusion and high melt strength with strong physical properties.
SABIC® HDPE F00950 is typically used for production of thin films with good strength and rigidity. The material contains anti-oxidants.
SABIC® HDPE F00950 resin is typically used for blown film extrusion and production of high strength grocery sacks, shopping bags and high quality thin films for multi wall sack liners and replacement for thin paper products.
SABIC® HDPE F00950 can be extruded on conventional HMW-HDPE equipment with temperature settings between 200 and 220°C. Film properties have been measured at 25 µm films with a BUR = 4.Film has been produced on Kiefel IBC film blown line at 160 kg/h with a die of 150 mm, die gap of 1.2 mm and a frostline height of 150 cm (= 10D).
This product is not intended for and must not be used in any pharmaceutical/medical applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 抗氧化高熔体强度 | |||
| 添加助剂 | 抗氧化剂 | |||
| 成型方式 | 挤出吹塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.95 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.07 g/10min | ISO 1133 | |
190℃/5 kg | 0.3 g/10 min | ISO 1133 | |
190℃/21.6 kg | 8.5 g/10 min | ISO 1133 | |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 30 Mpa | ISO 527-3 | |
屈服(yld) | 30 Mpa | ISO 527-3 | |
断裂(brk) | 40 Mpa | ISO 527-3 | |
断裂(brk) | 50 Mpa | ISO 527-3 | |
拉伸延伸率 | |||
断裂(brk) | 300 % | ISO 527-3 | |
断裂(brk) | 400 % | ISO 527-3 | |
埃尔曼多夫撕裂 | 6 N/mm | ISO 6383-2 | |
埃尔曼多夫撕裂 | 20 N/mm | ISO 6383-2 | |
落锤冲击 | 35 J/mm | ASTM D4272 | |
弹性模量 | 620 MPa | ISO 527-3 | |
弹性模量 | 620 MPa | ISO 527-3 |