Marlex® HXM 50100
HDPE
雪佛龙菲利普斯(Chevron Phillips)
产品描述
This extra high molecular weight, ethylene-hexene copolymer is tailored for large blow molded and thermoformed parts that require:
• Good melt strength
• Good rigidity
• Exceptional ESCR
• Excellent low temperature impact strength
• Durability
Typical blow molded applications for HXM 50100 include:
• Shipping containers • Jerry cans • Fuel containers • Agricultural chemical tanks
Typical thermoformed applications for HXM 50100 include:
• Pallets • Automotive dunnage • Truck bedliners • Playground equipment
This resin meets these specifications:
• ASTM D4976 - PE 235
• FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per Table 2 of 21 CFR 176.170(c)
• UL94HB yellow card per UL file E349283
• NSF Standard 61 for potable water
• Listed in the Drug Master File
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高耐久性耐低温冲击食品接触级饮用水级ESCR高熔体强度 | |||
| 法规认证 | ASTM D4976(聚乙烯注塑和挤压材料标准)DMF(药品主控文件)FDA(食品药品监督管理局)NSF(美国卫生基金会食品认证) | |||
| 成型方式 | 吹塑热成型 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.948 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 10 g/10min | ASTM D1238 | |
环境应力开裂(ESCR ) | 1000 Hours | ASTM D 1693 | Condition B (100 % Igepal), F50 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 25 Mpa | ASTM D638 | 2 in/min, Type IV bar |
拉伸延伸率 | |||
断裂(brk) | 700 % | ASTM D638 | 2 in/min, Type IV bar |
弯曲模量 | 1200 Mpa | ASTM D790 | Tangent - 16:1 span:depth, 0.5 in/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸冲击 | 190 kJ/m² | ASTM D 1822 | Type S bar |
脆化温度 | -75 °C | ASTM D 746 | Type A, Type I specimen |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 68 D | ASTM D 2240 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 78 °C | ASTM D648 | Method A |
维卡软化温度(Vicat) | 126 °C | ASTM D1525 | Loading 1, Rate A |