Hostalen GM 5010 T3 BLACK
HDPE
利安德巴塞尔(LyondellBasell)
产品描述
Hostalen GM 5010 T3 black is a high density polyethylene (HDPE), black colored similar RAL 9004 with high melt viscosity for extrusion, injection and compression moulding. The product is classified as PE 80 and provides excellent stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength.
This grade is not intended for medical and pharmaceutical applications.
This grade is supported for use in drinking water applications.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 耐热老化耐磨抗蠕变易焊接饮用水级抗紫外线耐候性ESCR耐化学性高粘度 | |||
| 颜色形状 | 黑色 | |||
| 成型方式 | 注塑挤出模压 | |||
| 增强填充 | 2.25% 炭黑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.957 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
190℃/5 kg | 0.43 g/10 min | ISO 1133 | |
190℃/21.6 kg | 9 g/10 min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 22 Mpa | ISO 527-1/-2 | 23 °C, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 8 % | ISO 527-1/-2 | 23 °C, 50 mm/min |
断裂(brk) | 350 % | ISO 527-1/-2 | 23 °C |
拉伸模量 | 1050 Mpa | ISO 527-1/-2 | 23 °C |
拉伸蠕变模量 | |||
1h | 640 Mpa | ISO 899-1 | 2 MPa |
1000h | 300 Mpa | ISO 899-1 | 2 MPa |
弯曲蠕变模量 | 1000 Mpa | DIN 16841 | 4-point loading / 1 min |
弯曲蠕变模量 | 300 Mpa | DIN 16841 | 4-point loading / 2000 hr |
弯曲蠕变模量 | 470 Mpa | DIN 16841 | 4-point loading / 24 hr |
全缺口蠕变试验(FNCT) | 100 hr | ISO 16770 | 4.0 MPa, 2% Arkopal N100, 80 °C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 8 kJ/m² | ISO 179-1/1eA | |
23℃ (73℉) | 24 kJ/m² | ISO 179-1/1eA | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 59 D | ISO 868 | 3 sec |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 70 °C | ISO 306/B50 | |
熔融温度(Tm) | 129 °C | DSC | |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
氧化诱导期(OIT) | 30 Min | ISO 11357 | 210 °C |
最小环向张应力强度(MRS) | 8 Mpa | ISO 9080 | |
嗅觉阈 | 2 - | EN 1622/EN 1420 | measured on pellets / 30°C / 4 h extraction time |