Ultrathene UE637000
EVA
利安德巴塞尔(LyondellBasell)
产品描述
Ultrathene UE637000 is an EVA copolymer with good toughness, flexibility and clarity. Typical applications include laminating and heavy duty films as well as injection and blow molding.
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 成型方式 | 流延薄膜注塑片材挤出型材挤出吹塑吹膜挤出吹塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 3.2 g/10min | ASTM D1238 | |
醋酸乙烯(VA)含量 | 9 % | Internal | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
脆化温度 | -76 °C | ASTM D 746 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 A | 94 A | ASTM D 2240 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 80 °C | ASTM D1525 | |
加工温度 | 232 °C | - | Max. melt temperature |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 6.2 Mpa | ASTM D 882 | MD |
屈服(yld) | 5.8 Mpa | ASTM D 882 | TD |
断裂(brk) | 26.2 Mpa | ASTM D 882 | MD |
断裂(brk) | 18.6 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
屈服(yld) | 9 % | ASTM D 882 | MD |
屈服(yld) | 11 % | ASTM D 882 | TD |
断裂(brk) | 350 % | ASTM D 882 | MD |
断裂(brk) | 500 % | ASTM D 882 | TD |
割线模量 | 84.8 Mpa | ASTM D 882 | MD, 1% Secant Modulus |
割线模量 | 91 Mpa | ASTM D 882 | TD, 1% Secant Modulus |
落锤冲击 | 400 g | ASTM D 1709 | F50 |