Escorene™ Ultra LD 726.07
Escorene™ Ultra LD 726.07
EVA
埃克森美孚化工(ExxonMobil Chemical)
产品描述
LD726.07 is primarily designed for high speed/low coating weight extrusion coating and is a good coextrusion partner with other polymers. LD726.07 is an excellent sealing material with a very low seal initiation temperature and high clarity.
基本信息
| 原厂资料 | 物性表(英文) 物性表(中文) |
| 成型方式 | 挤出涂层 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 0.939 g/cm³
| ASTM D 1505 | |
熔体质量流动速率(MFR) | | | |
190℃/2.16 kg |
14 g/10min | ASTM D1238 | |
内缩量(Neck-in) | 11 cm
| Internal | 100 m/min, Constant output at 35 rpm, 230°C |
内缩量(Neck-in) | 9.5 cm
| Internal | 200 m/min, Constant output at 35 rpm, 230°C |
醋酸乙烯(VA)含量 | 18 %
| Internal | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 A | 90 A
| ASTM D 2240 | 15 sec |
邵氏硬度 D | 34 D
| ASTM D 2240 | 15 sec |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 55 °C
| ASTM D1525 | |
熔融温度(Tm) | 83 °C
| Internal | Peak |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
7.5 Mpa | ASTM D 882 | MD |
拉伸延伸率 | | | |
断裂(brk) |
800 % | ASTM D 882 | MD |