| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.06 g/cm3
| ISO 1183 | 23°C |
比重 | 1.06 g/cm3
| ASTM D792 | |
熔体质量流动速率(MFR) | | | |
220℃/10 kg |
15 g/10 min | ISO 1133 | |
220℃/10 kg |
15 g/10 min | ASTM D 1238 | |
230°C/3.8 kg |
3.9 g/10 min | ASTM D 1238 | |
230°C/3.8 kg |
3.9 g/10 min | ISO 1133 | |
收缩率 | | | |
纵向(Flow) |
0.4~0.8 % | ASTM D 955 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
43 Mpa | ASTM D638 | Flow, 23°C, Injection Molded, 50 mm/min |
屈服(yld) |
43.8 Mpa | ISO 527 | Flow, 23°C, Injection Molded |
弯曲模量 | 2180 Mpa
| ASTM D790 | Chord, Flow, 23°C, Injection Molded |
弯曲模量 | 2170 Mpa
| ISO 178 | Chord, Flow, 23°C, Injection Molded |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
-30℃ (-22℉) |
8.2 kJ/m2 | ISO 179 | Injection Molded |
23℃ (73℉) |
18 kJ/m2 | ISO 179 | Injection Molded |
悬臂梁缺口(Izod Notched) | | | |
-30℃ (-22℉) |
110 J/m | ASTM D256 | Injection Molded |
-30℃ (-22℉) |
7.8 kJ/m2 | ISO 180 | Injection Molded |
23℃ (73℉) |
260 J/m | ASTM D256 | Injection Molded |
23℃ (73℉) |
21 kJ/m2 | ISO 180 | Injection Molded |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 100 R
| ASTM D785 | 23°C, Injection Molded |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm2） |
89.2 °C | ASTM D648 | Unannealed, Injection Molded |
0.45 Mpa (66 psi)（4.6kg/cm2） |
89.3 °C | ISO 75-2/B | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm2） |
76.7 °C | ASTM D648 | Unannealed, 3.18 mm, Injection Molded |
1.8 Mpa (264 psi)（18.6kg/cm2） |
82.8 °C | ASTM D648 | Unannealed, 6.35 mm |
1.8 Mpa (264 psi)（18.6kg/cm2） |
76.6 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 102 °C
| ASTM D1525 | Loading 1 (10 N) |
维卡软化温度(Vicat) | 102 °C
| ISO 306 | |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
93 E-6 cm/cm/℃ | ISO 11359-2 | -30 to 80°C |
横向(Across Flow) |
98 E-6 cm/cm/℃ | ISO 11359-2 | -30 to 80°C |